Lactide copolymers and ring-opened lactide copolymers

ABSTRACT

A process of forming a lactide copolymer includes forming a dimethylidene lactide molecule from an L-lactide molecule. The process also includes forming a functionalized lactide monomer from the dimethylidene lactide molecule. The process includes forming a mixture that includes the functionalized lactide monomer and a bisphenol A (BPA) monomer or a BPA-derived monomer. The process further includes polymerizing the mixture to form a lactide copolymer.

BACKGROUND

Plastics are typically derived from a finite and dwindling supply of petrochemicals, resulting in price fluctuations and supply chain instability. Replacing non-renewable petroleum-based polymers with polymers derived from renewable resources may be desirable. However, there may be limited alternatives to petroleum-based polymers in certain contexts. To illustrate, particular plastics performance standards may be specified by a standards body or by a regulatory agency. In some cases, alternatives to petroleum-based polymers may be limited as a result of challenges associated with satisfying particular plastics performance standards.

SUMMARY

According to an embodiment, a process of forming a lactide copolymer is disclosed. The process includes forming a dimethylidene lactide molecule from an L-lactide molecule. The process also includes forming a functionalized lactide monomer from the dimethylidene lactide molecule. The process includes forming a mixture that includes the functionalized lactide monomer and a bisphenol A (BPA) monomer or a BPA-derived monomer. The process further includes polymerizing the mixture to form a lactide copolymer.

According to another embodiment, a process of forming a ring-opened lactide copolymer is disclosed. The process includes forming a dimethylidene lactide molecule from an L-lactide molecule. The process also includes forming a functionalized lactide monomer from the dimethylidene lactide molecule. The process includes forming a mixture that includes the functionalized lactide monomer and a BPA monomer or a BPA-derived monomer. The process further includes polymerizing the mixture to form a lactide copolymer, and initiating a ring-opening polymerization reaction to form a ring-opened lactide copolymer from the lactide copolymer.

According to another embodiment, an article of manufacture is disclosed. The article of manufacture is formed by a process that includes forming a dimethylidene lactide molecule from an L-lactide molecule and forming a functionalized lactide monomer from the dimethylidene lactide molecule. The process also includes forming a mixture that includes the functionalized lactide monomer and a BPA monomer or a BPA-derived monomer. The process further includes polymerizing the mixture to form a lactide copolymer and initiating a ring-opening polymerization reaction to form a ring-opened lactide copolymer from the lactide copolymer. The process includes forming an article of manufacture from the ring-opened lactide copolymer.

The foregoing and other objects, features, and advantages of the invention will be apparent from the following more particular descriptions of exemplary embodiments of the invention as illustrated in the accompanying drawings wherein like reference numbers generally represent like parts of exemplary embodiments of the invention.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1A is a chemical reaction diagram illustrating an example of a process of forming a first functionalized lactide monomer that is derived from a dimethylidene lactide molecule, according to an embodiment.

FIG. 1B is a chemical reaction diagram illustrating an example of a process of utilizing the first functionalized lactide monomer of FIG. 1A to form a first lactide copolymer.

FIG. 1C is a chemical reaction diagram illustrating an example of a process of forming a first ring-opened lactide copolymer from the first lactide copolymer of FIG. 1B, according to one embodiment.

FIG. 2A is a chemical reaction diagram illustrating an example of a process of forming a second functionalized lactide monomer that is derived from a dimethylidene lactide molecule, according to an embodiment.

FIG. 2B is a chemical reaction diagram illustrating an example of a process of utilizing the first functionalized lactide monomer of FIG. 2A to form a second lactide copolymer.

FIG. 2C is a chemical reaction diagram illustrating an example of a process of forming a second ring-opened lactide copolymer from the second lactide copolymer of FIG. 2B, according to one embodiment.

FIG. 3A is a chemical reaction diagram illustrating an example of a process of forming a third functionalized lactide monomer that is derived from a dimethylidene lactide molecule, according to an embodiment.

FIG. 3B is a chemical reaction diagram illustrating an example of a process of utilizing the third functionalized lactide monomer of FIG. 3A to form a second lactide copolymer.

FIG. 3C is a chemical reaction diagram illustrating an example of a process of forming a third ring-opened lactide copolymer from the third lactide copolymer of FIG. 3B, according to one embodiment.

FIG. 4 is a flow diagram depicting a particular embodiment of a process of utilizing a functionalized lactide monomer derived from a dimethylidene lactide molecule to form a lactide copolymer.

FIG. 5 is a flow diagram depicted a particular embodiment of a process of utilizing a functionalized lactide monomer derived from a dimethylidene lactide molecule to form a lactide copolymer and utilizing the lactide copolymer to form a ring-opened lactide copolymer.

DETAILED DESCRIPTION

The present disclosure describes functionalized lactide monomers derived from a dimethylidene lactide molecule, lactide copolymers formed from the functionalized lactide monomers, and ring-opened lactide copolymers formed from the lactide copolymers. In the present disclosure, an L-lactide molecule may be utilized to form a dimethylidene lactide molecule. The exocyclic double bonds on the dimethylidene lactide (DML) molecule can undergo further functionalization to create lactide monomers with functional groups (also referred to herein as “functionalized lactide monomers”). In some cases, the functionalized lactide monomers may be polymerized with a bisphenol A (BPA) monomer or a BPA derivative monomer, such as bisphenol A diglycidyl ether (DGEBA), to form lactide copolymers. In other cases, the lactide copolymers may undergo ring-opening polymerization to form ring-opened lactide copolymers. While the present disclosure describes functionalization of DML molecules with epoxide groups and hydroxyl groups for subsequent formation of lactide copolymers, it will be appreciated that the DML molecules may be functionalized with alternative and/or additional groups. To illustrate, the functionalized lactide monomers of the present disclosure may include lactide monomers functionalized with vinyl group(s), amine group(s), anhydride(s), etc., among other alternatives.

Referring to FIG. 1A, a chemical reaction diagram 100 illustrates an example of a process of forming a first functionalized lactide monomer 102. FIG. 1B is a chemical reaction diagram 110 illustrating that, in some cases, the first functionalized lactide monomer 102 of FIG. 1A may be utilized to form a first lactide copolymer 112. FIG. 1C is a chemical reaction diagram 120 illustrating that, in some cases, the first lactide copolymer 112 of FIG. 1B may be utilized to form a first ring-opened lactide copolymer 122.

The first two chemical reactions depicted in FIG. 1A illustrate the formation of a dimethylidene lactide molecule from an L-lactide molecule. In a particular embodiment, formation of the dimethylidene lactide molecule may include radical bromination (depicted as Br₂, hv in FIG. 1A) in the presence to carbon tetrachloride (CCl₄). Subsequently, FIG. 1A illustrates that elimination with triethylamine (NEt₃) in a solvent such as dichloromethane (DCM) results in the formation of the dimethylidene lactide (DML) molecule.

As a prophetic example, the DML molecule may be formed by photobromination of the L-lactide molecule in a carbon tetrachloride (CCl₄) solution using a mercury vapor lamp (e.g., a H-100A-38-4 mercury vapor lamp from General Electric, Inc.). The dibrominated intermediate molecule may be dehydrobrominated by reaction with triethylamine (NEt₃) in a carefully dried ether. The resulting crude DML molecule may then be purified according to a purification procedure known to one of ordinary skill in the art.

The third chemical reaction depicted in FIG. 1A illustrates that the first functionalized lactide monomer 102 may be synthesized from the DML molecule. In a particular embodiment, the third chemical reaction of FIG. 1A may include chemically reacting 2-oxiranemethanethiol via a triethylamine-catalyzed Michael addition with DML to form the first functionalized lactide monomer 102, representing an example of a bisthioepoxide functionalized lactide molecule. As a prophetic example, to a solution of 2-Oxiranemethanethiol (2.1 eqiuv.), and triethylamine (0.3 equiv.) in anhydrous acetonitrile, may be added a solution of DML (1.0 equiv.) in anhydrous acetonitrile, dropwise at 0° C., under an inert atmosphere. The reaction mixture may be stirred for 1.5 hours at 0° C., and then concentrated by about 80% in vacuo. The concentrated solution may be dissolved in ethyl acetate and washed with 0.1 M HCl (×3), dried over MgSO₄, filtered, and the solvents removed in vacuo. The resulting solid may be purified by column chromatography or recrystallization.

Referring to FIG. 1B, a chemical reaction diagram 110 illustrates that the first functionalized lactide monomer 102 of FIG. 1A may be used to form a first lactide copolymer 112, representing a first example of a lactide-BPA copolymer. In a particular embodiment, the first functionalized lactide monomer 102 may be reacted with BPA under basic conditions (depicted as “B⁻” in FIG. 1B) to form the first lactide copolymer 112. In some cases, the first lactide copolymer 112 of FIG. 1B may be used in resins. In other cases, the first lactide copolymer 112 of FIG. 1B may be reacted further to make a cross-linked poly(lactic acid) network, as illustrated and described further herein with respect to FIG. 1C.

Referring to FIG. 1C, a chemical reaction diagram 120 illustrates an example of a process of forming a first ring-opened lactide copolymer 122 from the first lactide copolymer 112 of FIG. 1B. In the example of FIG. 1C, synthesis of the first ring-opened lactide copolymer 122 may include reacting the first lactide copolymer 112 with a tin(II) octanoate material (depicted as “Sn(OC₈H₁₇)₂” in FIG. 1C) under ring-opening polymerization conditions. The first ring-opened lactide copolymer 122 of FIG. 1C represents a first example of a cross-linked polymer that may be utilized as a renewable alternative for epoxy thermoset resins, such as coatings, electrical insulators, fiber-reinforced plastics, and structural adhesives, among other alternatives. In some cases, formulation of such a renewable thermoset material may take place before the cross-linking reaction depicted in FIG. 1C in order to incorporate additives, plasticizers, fillers, or combinations thereof (among other alternatives). Further, it will be appreciated that the first lactide copolymer 112 of FIG. 1B also includes free hydroxyl groups that can also be cross-linked further with other epoxy groups, isocyanates, carbonates, esters, etc. to from alternative thermoset materials.

Thus, FIGS. 1A-1C illustrate an example of a process of forming a functionalized lactide monomer and utilizing the functionalized lactide monomer to form a lactide copolymer (e.g., a BPA-lactide copolymer) or a ring-opened lactide copolymer. While not shown in the example of FIGS. 1A-1C, the lactide copolymers and/or ring-opened lactide copolymers may be utilized to form various articles of manufacture. As an example, the BPA-lactide copolymer depicted in FIG. 1B (prior to ring-opening polymerization) may be used in resins. As another example, the ring-opened BPA-lactide copolymer of FIG. 1C may be utilized as a renewable alternative for epoxy thermoset resins, such as coatings, electrical insulators, fiber-reinforced plastics, and structural adhesives, among other alternatives.

Referring to FIG. 2A, a chemical reaction diagram 200 illustrates an example of a process of forming a second functionalized lactide monomer 202. FIG. 2B is a chemical reaction diagram 210 illustrating that, in some cases, the first functionalized lactide monomer 202 of FIG. 2A may be utilized to form a second lactide copolymer 212. FIG. 2C is a chemical reaction diagram 220 illustrating that, in some cases, the second lactide copolymer 212 of FIG. 2B may be utilized to form a second ring-opened lactide copolymer 222.

The first two chemical reactions depicted in FIG. 2A illustrate the formation of a dimethylidene lactide molecule from an L-lactide molecule. The process of forming the dimethylidene lactide molecule may be similar to the process previously described herein with respect to FIG. 1A.

The second chemical reaction depicted in FIG. 2A illustrates that the second functionalized lactide monomer 202 may be synthesized from the DML molecule. In a particular embodiment, the second chemical reaction of FIG. 2A may include chemically reacting the DML molecule under hydroboration conditions to form the second functionalized lactide monomer 202, representing an example of a diol functionalized lactide molecule. While not shown in the example of FIG. 2A, in some cases, a protecting group may be utilized for the hydroxyl groups of the second functionalized lactide monomer 202. As a prophetic example, 9-BBN (0.5 M in THF, 2.1 equiv.) may be added dropwise over 30 min to a stirred and cooled (0° C.) solution of DML (1.0 equiv.) in THF (125 mL). The ice bath may be removed, and stirring may continue for 12 hours. The mixture may be cooled to 0° C. and quenched by dropwise addition of MeOH. Aqueous NaOH (2 M, >1.5 equiv.) and 30% H₂O₂ (>10.0 equiv.) may be poured into the stirred mixture. Stirring may be continued for 2 hours, and the mixture may be extracted with Et₂O. The combined organic extracts may be washed with brine, dried over Na₂SO₄, and the solvent may be removed in vacuo. The crude product may be purified through column chromatography.

Referring to FIG. 2B, a chemical reaction diagram 210 illustrates that the second functionalized lactide monomer 202 of FIG. 2A may be used to form a second lactide copolymer 212, representing a first example of a lactide-DGEBA copolymer. While FIG. 2A illustrates a particular embodiment in which the BPA derivative includes DGEBA, it will be appreciated that other di-functional epoxides may also be utilized. As an illustrative, non-limiting example, an alternative bis-epoxy material may include a cycloaliphatic diepoxide, such as ERL-4221 (3,4-Epoxycyclohexanemethyl 3,4-epoxycyclohexanecarboxylate), among other alternatives. In a particular embodiment, the second functionalized lactide monomer 202 may be reacted with DGEBA under basic conditions (depicted as “B⁻” in FIG. 2B) to form the second lactide copolymer 212. In some cases, the second lactide copolymer 212 of FIG. 2B may be used in resins. In other cases, the second lactide copolymer 212 of FIG. 2B may be reacted further to make a cross-linked poly(lactic acid) network, as illustrated and described further herein with respect to FIG. 2C.

Referring to FIG. 2C, a chemical reaction diagram 220 illustrates an example of a process of forming a second ring-opened lactide copolymer 222 from the second lactide copolymer 212 of FIG. 2B. In the example of FIG. 2C, synthesis of the second ring-opened lactide copolymer 222 may include reacting the first lactide copolymer 212 with a tin(II) octanoate material (depicted as “Sn(OC₈H₁₇)₂” in FIG. 2C) under ring-opening polymerization conditions. The second ring-opened lactide copolymer 222 of FIG. 2C represents a first example of a cross-linked polymer that may be utilized as a renewable alternative for epoxy thermoset resins, such as coatings, electrical insulators, fiber-reinforced plastics, and structural adhesives, among other alternatives. In some cases, formulation of such a renewable thermoset material may take place before the cross-linking reaction depicted in FIG. 2C in order to incorporate additives, plasticizers, fillers, or combinations thereof (among other alternatives). Further, it will be appreciated that the second lactide copolymer 212 of FIG. 2B also includes free hydroxyl groups that can also be cross-linked further with other epoxy groups, isocyanates, carbonates, esters, etc. to from alternative thermoset materials.

Thus, FIGS. 2A-2C illustrate an example of a process of forming a functionalized lactide monomer and utilizing the functionalized lactide monomer to form a lactide copolymer (e.g., a DGEBA-lactide copolymer) or a ring-opened lactide copolymer. While not shown in the example of FIGS. 2A-2C, the lactide copolymers and/or ring-opened lactide copolymers may be utilized to form various articles of manufacture. As an example, the DGEBA-lactide copolymer depicted in FIG. 2B (prior to ring-opening polymerization) may be used in resins. As another example, the ring-opened DGEBA-lactide copolymer of FIG. 2C may be utilized as a renewable alternative for epoxy thermoset resins, such as coatings, electrical insulators, fiber-reinforced plastics, and structural adhesives, among other alternatives.

Referring to FIG. 3A, a chemical reaction diagram 300 illustrates an example of a process of forming a third functionalized lactide monomer 302. FIG. 3B is a chemical reaction diagram 310 illustrating that, in some cases, the third functionalized lactide monomer 302 of FIG. 3A may be utilized to form a third lactide copolymer 312. FIG. 3C is a chemical reaction diagram 320 illustrating that, in some cases, the third lactide copolymer 312 of FIG. 3B may be utilized to form a third ring-opened lactide copolymer 322.

The first two chemical reactions depicted in FIG. 3A illustrate the formation of a dimethylidene lactide molecule from an L-lactide molecule. The process of forming the dimethylidene lactide molecule may be similar to the process previously described herein with respect to FIG. 1A. The third chemical reaction depicted in FIG. 3A illustrates that the third functionalized lactide monomer 302 may be synthesized from the DML molecule. In a particular embodiment, the third chemical reaction of FIG. 3A may include chemically reacting meta-chloroperbenzoic acid (MCPBA) with DML to form the third functionalized lactide monomer 302, representing an example of a bisepoxide-functionalized lactide molecule. As a prophetic example, MCPBA (meta-chloroperbenzoic acid, >2.0 equiv) and DML (1.0 equiv.) may be dissolved in dichloromethane. The reaction mixture may be heated with stirring, under reflux, for 24 hours. After completion, the mixture may be washed with a saturated solution of sodium bicarbonate and 10% aqueous sodium bisulfite. Subsequently, the organic phase may be dried over magnesium sulfate, filtered, and the solvents may be removed in vacuo. The resulting solid may be purified by recrystallization or column chromatography.

Referring to FIG. 3B, a chemical reaction diagram 310 illustrates that the third functionalized lactide monomer 302 of FIG. 3A may be used to form a third lactide copolymer 312, representing a second example of a lactide-BPA copolymer (that is different from the lactide-BPA copolymer depicted in FIG. 1B). In a particular embodiment, the third functionalized lactide monomer 302 may be reacted with BPA under basic conditions (depicted as “B⁻” in FIG. 3B) to form the third lactide copolymer 312. In some cases, the third lactide copolymer 312 of FIG. 3B may be used in resins. In other cases, the third lactide copolymer 312 of FIG. 3B may be reacted further to make a cross-linked poly(lactic acid) network, as illustrated and described further herein with respect to FIG. 3C.

Referring to FIG. 3C, a chemical reaction diagram 320 illustrates an example of a process of forming a third ring-opened lactide copolymer 322 from the third lactide copolymer 312 of FIG. 3B. In the example of FIG. 3C, synthesis of the third ring-opened lactide copolymer 322 may include reacting the third lactide copolymer 312 with a tin(II) octanoate material (depicted as “Sn(OC₈H₁₇)₂” in FIG. 3C) under ring-opening polymerization conditions. The third ring-opened lactide copolymer 322 of FIG. 3C represents a third example of a cross-linked polymer that may be utilized as a renewable alternative for epoxy thermoset resins, such as coatings, electrical insulators, fiber-reinforced plastics, and structural adhesives, among other alternatives. In some cases, formulation of such a renewable thermoset material may take place before the cross-linking reaction depicted in FIG. 3C in order to incorporate additives, plasticizers, fillers, or combinations thereof (among other alternatives). Further, it will be appreciated that the third lactide copolymer 312 of FIG. 3B also includes free hydroxyl groups that can also be cross-linked further with other epoxy groups, isocyanates, carbonates, esters, etc. to from alternative thermoset materials.

Thus, FIGS. 3A-3C illustrate an example of a process of forming a functionalized lactide monomer and utilizing the functionalized lactide monomer to form a lactide copolymer (e.g., a BPA-lactide copolymer) or a ring-opened lactide copolymer. While not shown in the example of FIGS. 3A-3C, the lactide copolymers and/or ring-opened lactide copolymers may be utilized to form various articles of manufacture. As an example, the BPA-lactide copolymer depicted in FIG. 3B (prior to ring-opening polymerization) may be used in resins. As another example, the ring-opened BPA-lactide copolymer of FIG. 3C may be utilized as a renewable alternative for epoxy thermoset resins, such as coatings, electrical insulators, fiber-reinforced plastics, and structural adhesives, among other alternatives.

Referring to FIG. 4, a flow diagram illustrates a particular embodiment of a process 400 of utilizing a functionalized lactide monomer derived from a dimethylidene lactide molecule to form a lactide copolymer. While not shown in the example of FIG. 4, the process 400 may further include forming an article of manufacture from the lactide copolymer (e.g., a resin material).

The process 400 includes forming a dimethylidene lactide molecule from an L-lactide molecule, at 402. For example, referring to FIG. 1A, the dimethylidene lactide molecule may be formed from the L-lactide molecule by radical bromination of the L-lactide molecule, followed by elimination with triethylamine (NEt₃).

The process 400 includes forming a functionalized lactide monomer from the dimethylidene lactide molecule, at 404. For example, referring to FIG. 1A, the dimethylidene lactide molecule may be utilized to form the first functionalized lactide monomer 102, representing an example of a bisthioepoxide-functionalized lactide monomer. As another example, referring to FIG. 2A, the dimethylidene lactide molecule may be utilized to form the second functionalized lactide monomer 202, representing an example of a diol-functionalized lactide monomer. As another example, referring to FIG. 3A, the dimethylidene lactide molecule may be utilized to form the third functionalized lactide monomer 302, representing an example of a bisepoxide-functionalized lactide monomer.

The process 400 includes forming a mixture that includes the functionalized lactide monomer and a BPA monomer or a BPA-derived monomer, at 406. The process 400 also includes polymerizing the mixture to form a lactide copolymer, at 408.

As an example, referring to FIG. 1B, the first functionalized lactide monomer 102 of FIG. 1A may be reacted with BPA under basic conditions (depicted as “B⁻” in FIG. 1B) to form the first lactide copolymer 112. In some cases, the first lactide copolymer 112 of FIG. 1B may be used to form an article of manufacture that includes a resin material. In other cases, as illustrated and further described herein with respect to FIG. 5, the first lactide copolymer 112 of FIG. 1B may be used to form the ring-opened lactide copolymer 122 of FIG. 1C.

As another example, referring to FIG. 2B, the second functionalized lactide monomer 202 of FIG. 2A may be reacted with DGEBA under basic conditions (depicted as “B⁻” in FIG. 2B) to form the second lactide copolymer 212. In some cases, the second lactide copolymer 212 of FIG. 2B may be used to form an article of manufacture that includes a resin material. In other cases, as illustrated and further described herein with respect to FIG. 5, the second lactide copolymer 212 of FIG. 2B may be used to form the ring-opened lactide copolymer 222 of FIG. 2C.

As yet another example, referring to FIG. 3B, the third functionalized lactide monomer 302 of FIG. 3A may be reacted with BPA under basic conditions (depicted as “B⁻” in FIG. 3B) to form the third lactide copolymer 312. In some cases, the third lactide copolymer 312 of FIG. 3B may be used to form an article of manufacture that includes a resin material. In other cases, as illustrated and further described herein with respect to FIG. 5, the third lactide copolymer 312 of FIG. 3B may be used to form the ring-opened lactide copolymer 322 of FIG. 3C.

Thus, FIG. 4 illustrates an example of a process of utilizing a functionalized lactide monomer derived from a dimethylidene lactide molecule to form a lactide copolymer. As illustrated and further described herein with respect to FIG. 5, in some cases, the lactide copolymer may be subsequently utilized to form a ring-opened lactide copolymer.

Referring to FIG. 5, a flow diagram illustrates a particular embodiment of a process 500 of utilizing the lactide copolymer formed according to the process 400 depicted in FIG. 4 to form a ring-opened lactide copolymer. In the particular embodiment depicted in FIG. 5, the process 500 further includes forming an article of manufacture from the ring-opened lactide copolymer.

The process 500 includes forming a functionalized lactide monomer from a dimethylidene lactide molecule (that is formed from a renewable L-lactide molecule), at 502.

For example, referring to FIG. 1A, the dimethylidene lactide molecule may be utilized to form the first functionalized lactide monomer 102, representing an example of a bisthioepoxide-functionalized lactide monomer. As another example, referring to FIG. 2A, the dimethylidene lactide molecule may be utilized to form the second functionalized lactide monomer 202, representing an example of a diol-functionalized lactide monomer. As another example, referring to FIG. 3A, the dimethylidene lactide molecule may be utilized to form the third functionalized lactide monomer 302, representing an example of a bisepoxide-functionalized lactide monomer.

The process 500 includes forming a mixture that includes the functionalized lactide monomer and a BPA monomer or a BPA-derived monomer, at 504. The process 500 also includes polymerizing the mixture to form a lactide copolymer, at 506.

As an example, referring to FIG. 1B, the first functionalized lactide monomer 102 of FIG. 1A may be reacted with BPA under basic conditions (depicted as “B⁻” in FIG. 1B) to form the first lactide copolymer 112. As another example, referring to FIG. 2B, the second functionalized lactide monomer 202 of FIG. 2A may be reacted with DGEBA under basic conditions (depicted as “B⁻” in FIG. 2B) to form the second lactide copolymer 212. As yet another example, referring to FIG. 3B, the third functionalized lactide monomer 302 of FIG. 3A may be reacted with BPA under basic conditions (depicted as “B⁻” in FIG. 3B) to form the third lactide copolymer 312.

The process 500 further includes forming a ring-opened lactide copolymer from the lactide copolymer, at 508. As an example, referring to FIG. 1C, the first lactide copolymer 112 may be utilized to form the first ring-opened lactide copolymer 122. As another example, referring to FIG. 2C, the second lactide copolymer 212 of FIG. 2B may be utilized to form the second ring-opened lactide copolymer 222. As yet another example, the third lactide copolymer 312 of FIG. 3B may be utilized to form the third ring-opened lactide copolymer 322.

In the particular embodiment depicted in FIG. 5, the process 500 further includes forming an article of manufacture that includes the ring-opened lactide copolymer, at 510. For example, the article of manufacture may include a renewable alternative for epoxy thermoset resins, such as coatings, electrical insulators, fiber-reinforced plastics, and structural adhesives, among other alternatives.

Thus, FIG. 5 illustrates an example of a process of utilizing the lactide copolymer formed according to the process described herein with respect to FIG. 4 to form a ring-opened lactide copolymer. FIG. 5 further illustrates that, in some cases, the ring-opened lactide copolymers of the present disclosure may be utilized to form articles of manufacture that represent renewable alternatives to some existing petroleum-derived materials.

It will be understood from the foregoing description that modifications and changes may be made in various embodiments of the present invention without departing from its true spirit. The descriptions in this specification are for purposes of illustration only and are not to be construed in a limiting sense. The scope of the present invention is limited only by the language of the following claims. 

What is claimed is:
 1. A compound having the following structural formula:


2. The compound of claim 1, wherein the compound reacts with a second monomer to form a lactide copolymer.
 3. The compound of claim 2, wherein the lactide copolymer participates in a reaction to form a ring-opened lactide copolymer.
 4. The compound of claim 2, wherein the second monomer is bisphenol A diglycidyl ether (DGEBA).
 5. The compound of claim 2, wherein the second monomer is bisphenol A (BPA).
 6. The compound of claim 2, wherein the lactide copolymer has the following structural formula:


7. The compound of claim 2, wherein the lactide copolymer participates in a reaction to form a copolymer having the following structural formula:


8. The compound of claim 2, wherein the lactide copolymer participates in a reaction to form a ring-opened lactide copolymer, and wherein the ring-opened lactide copolymer is cross-linked with moieties selected from the group consisting of epoxies, isocyanates, carbonates, esters, and combinations thereof.
 9. A compound having the following structural formula:


10. The compound of claim 9, wherein the compound reacts with a second monomer to form a lactide copolymer.
 11. The compound of claim 10, wherein the lactide copolymer participates in a reaction to form a ring-opened lactide copolymer.
 12. The compound of claim 10, wherein the second monomer is selected from the group consisting of bisphenol A (BPA) and BPA diglycidyl ether (DGEBA).
 13. The compound of claim 10, wherein the lactide copolymer has the following structural formula:


14. The compound of claim 10, wherein the lactide copolymer participates in a reaction to form a copolymer having the following structural formula:


15. The compound of claim 10, wherein the lactide copolymer participates in a reaction to form a ring-opened lactide copolymer, and wherein the ring-opened lactide copolymer is cross-linked with moieties selected from the group consisting of epoxies, isocyanates, carbonates, esters, and combinations thereof.
 16. A compound having the following structural formula:


17. The compound of claim 16, wherein the compound reacts with a second monomer to form a lactide copolymer.
 18. The compound of claim 17, wherein the lactide copolymer has the following structural formula:


19. The compound of claim 17, wherein the lactide copolymer participates in a reaction to form a ring-opened lactide copolymer.
 20. The compound of claim 17, wherein the lactide copolymer participates in a reaction to form a ring-opened lactide copolymer, and wherein the ring-opened lactide copolymer is cross-linked. 